| Component - Plastics | E41797 |
| TORAY INDUSTRIES INC | |
| NIHONBASHI-MITSUI TOWER, 1-1 NIHONBASHI-MUROMACHI 2-CHOME, CHUO-KU, Tokyo 103-8666 Japan | |
| A504X90, A504X95, A504FG1, A504, A504CX1, A504CX2 (R) | |
| Polyphenylene Sulfide (PPS) "Torelina", furnished as pellets |
|
Color
|
Min. Thk
(mm)
|
Flame
Class
|
HWI
(PLC)
|
HAI
(PLC)
|
GWIT
(°C)
|
GWFI
(°C)
|
RTI Elec
(°C)
|
RTI Imp
(°C)
|
RTI Str
(°C)
|
|---|---|---|---|---|---|---|---|---|---|
| ALL | 0.28 | V-0 | -- | -- | -- | -- | 130 | 130 | 130 |
| 0.71 | V-0 | 1 | 1 | -- | -- | 200 | 200 | 200 | |
| 1.5 | V-0 | 0 | 1 | -- | -- | 220 | 200 | 210 | |
| 3.0 | V-0 | 0 | 0 | -- | -- | 220 | 200 | 210 |
| Comparative Tracking Index (CTI) (PLC): | 4 | IEC Comparative Tracking Index (V): | -- | IEC CTI Material Group: | -- |
| Inclined Plane Tracking (IPT) (kV): | -- | High-Voltage Arc Tracking Rate (HVTR) (PLC): | 1 | Dielectric Strength (DS) (kV/mm): | 21 |
| Volume Resistivity (VR) (10x ohm cm): | 16 | Surface Resistivity (SR) (10x ohms/square): | -- | High Volt, Low Current Arc Resis (D495): | 5 |
| (R) - Virgin and regrind up to 50% by weight inclusive have the same V-0 flammability and tensile impact characteristics when used within the 130 C generic temperature limitation: no other properties for regrind 26-50% by wt. incl. have been determined. |
| ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL. |
| Report Date: 1994-07-14 |
| Last Revised: 2025-11-14 |
 |
| © 2026 UL Solutions |
| ISO/IEC Flammability Properties | Value | Test Method | |
| Flammability |
IEC 60695-11-10
|
||
|
0.28 mm, Color: ALL
|
V-0
|
|
|
|
0.71 mm, Color: ALL
|
V-0
|
|
|
|
1.5 mm, Color: ALL
|
V-0
|
|
|
|
3.0 mm, Color: ALL
|
V-0
|
|